MICROPOROUS POLYOLEFIN MEMBRANE AND SEPARATOR FOR NONAQUEOUS ELECTROLYTE SECONDARY BATTERIES

The present invention relates to a microporous polyolefin membrane which has a shrinkage ratio of less than 10% in the MD direction at 105°C/8h and a fibril diameter of from 10 nm to 50 nm, wherein if a 11.7 μm × 9.4 μm rectangular field of view of a surface SEM observation image as obtained by the observation with a scanning electron microscope (SEM) is divided into 0.5 μm × 0.5 μm pieces, the sum of resin areas in the pieces satisfying R2 ≥ R1, namely (non-opening parts a in the surface) is 20 μm2 or less in the 11.7 μm × 9.4 μm area of the surface SEM observation image. La présente invention concerne une membrane de polyoléfine microporeuse qui présente un taux de retrait inférieur à 10 % dans le sens MD à 105 °C/8h et un diamètre de fibrilles de 10 nm à 50 nm, dans laquelle si un champ de vision rectangulaire de 11,7 μm × 9,4 μm d'une image d'observation par MEB de surface telle qu'obtenue par l'observation avec un microscope électronique à balayage (MEB) est divisée en morceaux de 0,5 µm × 0,5 µm, la somme des surfaces de résine dans les pièces satisfaisant à R2 ≥ R1, à savoir (parties a non ouvrable dans la surface) est inférieure ou égale à 20 μm2 dans la surface de 11,7 μm × 4 μm de l'image d'observation par MEB de surface. 本発明は、１０５℃／８ｈのＭＤ方向の収縮率が１０％未満であり、走査型電子顕微鏡（ＳＥＭ）を用いた観察により得られる表面ＳＥＭ観察画像１１．７μｍ×９．４μｍの長方形状の視野を縦横それぞれ０．５μｍ画に分割し、Ｒ２≧Ｒ１の関係を満たす区画中の樹脂面積の総和（表面の未開孔部ａ）が、前記表面ＳＥＭ観察画像１１．７μｍ×９．４μｍにおいて２０μｍ２以下であり、フィブリル径が１０～５０ｎｍであるポリオレフィン微多孔膜に関する。