METHOD FOR PRODUCING LEAD ACID BATTERIES

Under constant voltage recharge, as occurs in battery applications, the recharge current drops if the Nernst voltage equals the applied voltage. Therefore, lead acid batteries cannot achieve optimal cycle life or rechargeability. The main reason is the increase of the Nernst voltage due to build-up of the specific gravity of the sulfuric acid, which increases more quickly in the positive electrode than in the negative electrode. The invention shows that specific alkaline silicates and/or alkaline zeolites act as blocker of the quick increase in sulfuric acid activity in the positive electrode. This is due to the fact that the cavities and alkaline atoms capture the sulphate ions and thereby reduce the sulfuric acid activity. Especially highly agglomerated alkaline aluminum silicates and alkaline aluminum zeolites are of special interest. Sous une recharge de tension constante, comme cela se produit dans des batteries, le courant de recharge chute si la tension de Nernst est égale à la tension appliquée. Par conséquent, les batteries au plomb/acide ne peuvent pas atteindre une durée de vie ou une capacité de recharge optimale. La raison principale est l'augmentation de la tension de Nernst due à l'accumulation de la gravité spécifique de l'acide sulfurique, qui augmente plus rapidement dans l'électrode positive que dans l'électrode négative. L'invention montre que des silicates alcalins et/ou des zéolites alcalines spécifiques agissent en tant que bloqueur de l'augmentation rapide de l'activité d'acide sulfurique dans l'électrode positive. Cela est dû au fait que les cavités et les atomes alcalins capturent les ions sulfate et réduisent ainsi l'activité d'acide sulfurique. En particulier, les silicates d'aluminium alcalin hautement agglomérés et les zéolites d'aluminium alcalines présentent un intérêt particulier.