AUSTENITIC STAINLESS STEEL POWDER COMPOSITION WITHOUT NICKEL AND PART MADE BY SINTERING BY MEANS OF SAID POWDER

The present invention relates to an austenitic stainless steel powder with a nickel content that is less than or equal to 0.5% by weight and a specific carbon content that is greater than or equal to 0.05% and less than or equal to 0.11% by weight. It also relates to a method for manufacturing said powder by powder metallurgy, and to the part (3) resulting from the manufacturing method which has the feature of having a deoxidized layer (1) on the surface of the part (3) that extends along a thickness e that is greater than or equal to 200 μm. La présente invention concerne une poudre d'acier inoxydable austénitique ayant une teneur en nickel inférieure ou égale à 0.5% en poids et une teneur en carbone spécifique qui est supérieure ou égale à 0.05% et inférieure ou égale à 0.11 % en poids. Elle se rapporte également au procédé de fabrication par métallurgie des poudres de cette poudre et à la pièce (3) issue du procédé de fabrication ayant pour caractéristique de présenter une couche désoxydée (1) en surface de la pièce (3) s'étendant sur une épaisseur e supérieure ou égale à 200 μm.