METHOD FOR PRODUCING ARAMID PAPER

A method for producing aramid paper that involves performing a hot-pressing step of mixing short aramid fibers and aramid fibrids in a mass ratio of 60/40 to 10/90 and forming a sheet, sandwiching the sheet obtained between a pair of heating elements, and applying a pressure of at least 500 kg/cm2 at least two times, wherein the hot-pressing step that is performed at least two times comprises a hot-pressing step (a) at a temperature exceeding the glass transition temperature of aramid and a hot-pressing step (b) performed thereafter at a temperature less than the glass transition temperature of aramid. L'invention concerne un procédé de production de papier aramide qui consiste à effectuer une étape de pressage à chaud en mélangeant des fibres d'aramide courtes et des fibrides d'aramide dans un rapport de masse de 60/40 à 10/90 et en formant une feuille, en prenant en sandwich la feuille obtenue entre une paire d'éléments chauffants, et en appliquant une pression d'au moins 500 kg/cm2 au moins deux fois, l'étape de pressage à chaud réalisée au moins deux fois comprenant une étape de pressage à chaud (a) à une température supérieure à la température de transition vitreuse de l'aramide et une étape de pressage à chaud (b) effectuée ensuite à une température inférieure à la température de transition vitreuse de l'aramide. アラミド短繊維及びアラミドファイブリッドを６０／４０～１０／９０の質量比で混合してシート状物を形成し、得られたシート状物を一対の発熱体の間に挟み、５００ｋｇ／ｃｍ2以上の圧力を加える熱圧加工処理工程を少なくとも２回行うことを含むアラミド紙の製造方法であって、少なくとも２回行う熱圧加工処理工程が、アラミドのガラス転移温度を超える温度での熱圧加工処理工程(a)及び、その後に行う、アラミドのガラス転移温度未満の温度での熱圧加工処理工程(b)を含むアラミド紙の製造方法。