HIGH ELONGATION POLYOLEFIN COMPOSITION WITH GLASS FIBER

A thermoplastic composition comprising 40 to 95 wt% of a polyolefin comprising a homopolymer or a copolymer comprising at least 80 wt% of units derived from polymerization of ethylene, propylene, or a combination thereof; and 5 to 60 wt% of a glass fiber coated with a sizing composition, wherein the glass fiber does not adhere to the polyolefin matrix; preferably wherein an injection molded sample of the thermoplastic composition has a flexural modulus of greater than 2,000, a flexural strength of 60 MPa or less, a tensile modulus of greater than 2,000 MPa, a tensile strength of 45 MPa or less, and a tensile elongation at break of greater than 5% according to ASTM D638 at 23C. La présente invention concerne une composition thermoplastique comprenant de 40 à 95 % en poids d'une polyoléfine comportant un homopolymère ou un copolymère comprenant au moins 80 % en poids d'unités dérivées de la polymérisation de l'éthylène, du propylène, ou d'une combinaison de ceux-ci ; et de 5 à 60 % en poids d'une fibre de verre revêtue d'une composition d'encollage, la fibre de verre n'adhérant pas à la matrice de polyoléfine et, de préférence, un échantillon moulé par injection de la composition thermoplastique ayant un module de flexion supérieur à 2 000, une résistance à la flexion de 60 MPa ou moins, un module de traction supérieur à 2 000 MPa, une résistance à la traction de 45 MPa ou moins, et un allongement à la traction à la rupture supérieur à 5 % selon la norme ASTM D638 à 23 °C.