PHOTOREACTIVE COMPOSITION

Provided is a photoreactive composition which, even when used for producing a molded object that poorly transmits light, can be efficiently hardened to the deep portion thereof. The photoreactive composition comprises a vinyl monomer and a filler. When the photoreactive composition, which comprises a vinyl monomer and a filler, is poured into a test tube with a diameter of 0.6 cm and a height of 5 cm to a height of 3 cm from the bottom of the test tube, irradiated with light from above the test tube using an LED lamp having a center wavelength of 365 nm at a light intensity of 30 mW/cm2 for 360 seconds, and allowed to stand at 25°C for 24 hours, then the conversion into polymer of the vinyl monomer present in a position 1 cm above the bottom of the test tube is 90% or higher. L'invention concerne une composition photoréactive qui, même lorsqu'elle est utilisée pour produire un objet moulé qui transmet faiblement la lumière, peut être durcie efficacement jusqu'à la portion profonde de celle-ci. La composition photoréactive comprend un monomère vinylique et une charge. Lorsque la composition photoréactive, qui comprend un monomère vinylique et une charge, est versée dans un tube d'essai ayant un diamètre de 0,6 cm et une hauteur comprise entre 5 cm et 3 cm à partir du fond du tube de test, est irradiée avec de la lumière depuis le dessus du tube de test en utilisant une lampe à LED ayant une longueur d'onde centrale de 365 nm à une intensité lumineuse de 30 mW/cm2 pendant 360 secondes, puis est laissée au repos à 25 °C pendant 24 heures, alors la conversion en polymère du monomère vinylique présent à une position 1 cm au-dessus du fond du tube de test est de 90 % ou plus. 光透過し難い成形体を製造する場合においても、深部まで効率よく硬化させることができる光反応性組成物を提供する。 ビニルモノマーと、フィラーとを含み、直径０．６ｃｍ及び高さ５ｃｍの試験管に、ビニルモノマー及びフィラーを含む光反応性組成物を試験管の底部からの高さ３ｃｍまで注入し、３６５ｎｍの中心波長を有するＬＥＤランプを用いて光強度３０ｍＷ／ｃｍ２で３６０秒間、試験管の上方から光照射し、２５℃で２４時間静置した後の試験管の底部から１ｃｍの位置におけるビニルモノマーの重合率が、９０％以上である、光反応性組成物。