A METHOD FOR IMPROVING BOTH STRENGTH AND DUCTILITY OF A PRESS-HARDENING STEEL

A method of forming a shaped steel object, includes cutting a blank from an alloy composition. The alloy composition includes 0.1-1 wt. % carbon, 0.1-3 wt. % manganese, 0.1-3 wt. % silicon, 1-10 wt. % aluminum, and a balance being iron. The method also includes heating the blank to a temperature above a temperature at which austenite begins to form to generate a heated blank, transferring the heated blank to a die, forming the heated blank into a predetermined shape defined by the die to generate a shaped steel object, and decreasing the temperature of the shaped steel object to ambient temperature. The heating is performed under an atmosphere comprising at least one of an inert gas, a carbon (C)-based gas, and nitrogen (N2) gas. L'invention concerne un procédé de mise en forme d'un objet en acier façonné, qui consiste à découper une ébauche à partir d'une composition d'alliage. La composition d'alliage comprend 0,1 à 1 % en poids de carbone, 0,1 à 3 % en poids de manganèse, 0,1 à 3 % en poids de silicium, 1 à 10 % en poids d'aluminium, le reste étant constitué de fer. Le procédé consiste également à chauffer l'ébauche jusqu'à une température supérieure à la température à laquelle de l'austénite commence à se former pour produire une ébauche chauffée, à transférer l'ébauche chauffée vers une matrice, à mettre en forme l'ébauche chauffée pour lui donner une forme prédéterminée définie par la matrice pour produire un objet en acier façonné, et à faire baisser la température de l'objet en acier façonné jusqu'à la température ambiante. Le chauffage est réalisé sous une atmosphère comprenant au moins un gaz inerte, un gaz à base de carbone (C) et de l'azote gazeux (N2).