ALUMINA@LAYERED DOUBLE HYDROXIDE CORE@SHELL PARTICLES AND PROCESSES OF MAKING THEM

Processes of preparing a plurality of LDH-coated alumina particles (i.e. alumina@LDH core@shell particles) is described, in which the alumina core has an average particle size of ≥50 μm. The resulting LDH-coated alumina particles offer a plethora of advantages over smaller particle size (e.g. powder) core@LDH materials. In particular, the alumina@LDH core@shell materials of the invention are suitable for direct use in a variety of industrial applications, including as supports in fixed bed reactors or fluidized bed processes, thereby obviating the numerous disadvantages associated with pelletising smaller particle size (e.g. powder) core@LDH materials. L'invention concerne des procédés de préparation d'une pluralité de particules d'alumine revêtues de LDH (c'est-à-dire des particules noyau-enveloppe d'alumine-LDH), dans lesquelles le noyau d'alumine a une taille de particule moyenne ≥ 50 µm. Les particules d'alumine revêtues de LDH résultantes offrent une pluralité d'avantages par rapport à des matériaux noyau-LDH de taille de particule plus petite (par exemple, une poudre). En particulier, les matériaux noyau-enveloppe d'alumine-LDH de l'invention sont appropriés pour une utilisation directe dans une variété d'applications industrielles, y compris en tant que supports dans des réacteurs à lit fixe ou des procédés à lit fluidisé, ce qui permet d'éviter les nombreux inconvénients associés à la granulation de matériaux noyau-LDH de taille de particule plus petite (par exemple, une poudre).