6XXX ALUMINUM ALLOY SHEET PRODUCTS AND METHODS FOR MAKING THE SAME

The present disclosure relates to methods for producing new 6xxx aluminum alloy sheet products having tailored precipitate phase particle size distributions. The tailored precipitate phase particle size distributions may be produced by preparing a 6xxx aluminum alloy sheet for precipitate phase modification, and then modifying an initial precipitate phase particle size distribution of the material. The modifying may include heating the intermediate gauge strip to a temperature of from 440°C (825°F) to 500°C (932°F) and for a time sufficient to create a modified strip product having a modified (tailored) precipitate phase particle size distribution. The modified strip product may realize improved properties. La présente invention concerne des procédés de production de nouveaux produits de feuille d'alliage d'aluminium de la série 6xxx ayant des distributions de tailles de particules de phase de précipité sur mesure. Les distributions de tailles de particule de phase de précipité sur mesure peuvent être produites par préparation d'une feuille d'alliage d'aluminium de la série 6xxx pour une modification de phase de précipité, puis par modification d'une distribution de tailles de particule de phase de précipité initiale du matériau. La modification peut comprendre le chauffage de la bande d'épaisseur intermédiaire à une température comprise entre 440 °C (825 °F) et 500 °C (932 °F) et pendant une durée suffisante pour créer un produit de bande modifié ayant une distribution de tailles de particule de phase de précipité modifiée (sur mesure). Le produit de bande modifié peut présenter des propriétés améliorées.