PRECIPITATION STRENGTHENED METAL ALLOY ARTICLE HAVING UNIFORM STRENGTH

A metal alloy article having a combination of mechanical properties which are uniform across a cross-sectional area of the article is disclosed. The metal alloy is a precipitation hardenable alloy, such as an aluminum, copper, nickel, iron, or titanium alloy. In specific embodiments, the metal alloy is a copper-nickel-tin alloy with a nominal composition of Cu-15Ni-8Sn. The article is strengthened by process treatment steps including solution annealing, cold working, and precipitation hardening. The article has a constant cross-section along a length thereof with a minimum 0.2% offset yield strength of about 70 ksi. Cette invention concerne un article en alliage métallique ayant une combinaison de propriétés mécaniques qui sont uniformes sur une zone de section transversale de l'article. L'alliage métallique est un alliage durcissable par précipitation, tel qu'un alliage d'aluminium, de cuivre, de nickel, de fer ou de titane. Selon des modes de réalisation spécifiques, l'alliage métallique est un alliage cuivre-nickel-étain de composition nominale Cu-15Ni-8 Sn. L'article est renforcé par des étapes de traitement comprenant un recuit de mise en solution, un travail à froid et un durcissement par précipitation. L'article a une section transversale constante sur sa longueur avec une limite apparente d'élasticité avec une déformation permanente de 0,2 % minimum d'environ 70 ksi.