FIBER COATINGS WITH LOW MODULUS AND HIGH CRITICAL STRESS

Fiber coatings with low Young's modulus, high tear strength, and/or high critical stress are realized with coating compositions that include an oligomeric material formed from an isocyanate, a hydroxy acrylate compound and a polyol. The oligomeric material includes a polyether urethane acrylate and a di-adduct compound. The reaction mixture used to form the oligomeric material includes a molar ratio of isocyanate:hydroxy acrylate:polyol of n:m:p, where when p is 2, n is in the range from 3.0 to 5.0 and m is in the range from 1.50n - 3 to 2.50n - 5. Control of the n:m:p ratio leads to compositions that, when cured, provide coatings and cured products having high critical stress, high tear strength, and a high ratio of tear strength to Young's modulus. L'invention concerne des revêtements de fibres présentant un faible module d'Young, une résistance élevée à la déchirure et/ou une résistance critique élevée, réalisés à l'aide de compositions de revêtement qui comprennent un matériau oligomère formé à partir d'un isocyanate, d'un composé hydroxy acrylate et d'un polyol. Le matériau oligomère comprend un acrylate de polyéther-uréthanne et un composé di-adduit. Le mélange réactionnel utilisé pour former le matériau oligomère comprend une proportion en moles isocyanate:hydroxy acrylate:polyol de n:m:p, où, quand p vaut 2, n est compris dans la plage de 3,0 à 5,0, et m est compris dans la plage de 1,50n-3 à 2,50n-5. La régulation de la proportion n:m:p conduit à des compositions qui, après durcissement, donnent des revêtements et des produits durcis présentant une résistance critique élevée, une résistance élevée au cisaillement et un rapport élevé entre la résistance au cisaillement et le module d'Young.