METHOD FOR THE PRODUCTION OF ACTIVATED CARBON

Method for the production of activated carbon for the chemisorption of toxic substances contained in water, in which carbon is subjected to the carbonization process, and carbonized activated carbon is impregnated with a catalysts, consists in that impregnation solution containing copper or manganese or silver or zinc salts is introduced into activated carbon surface and then mixed to equalize the humidity of carbon and seasoned at room temperature for 1.5 up to 2.5 hours. Then impregnated activated carbon is dried at the temperature of 100°C to 150°C for 1.0 to 6.5 hours; subsequently, it is heated at the temperature from 180°C to 380°C for 1.5 to 2.5 hours. L'invention concerne un procédé de fabrication de charbon actif pour la chimisorption de substances toxiques contenues dans l'eau ; dans ce procédé, du carbone est soumis au processus de carbonisation, et du charbon actif carbonisé est imprégné avec un catalyseur ; le procédé consiste en ce qu'une solution d'imprégnation contenant des sels de cuivre ou de manganèse ou d'argent ou de zinc est introduite dans une surface de charbon actif, puis mélangée pour égaliser l'humidité du carbone et séchée à la température ambiante pendant 1,5 jusqu'à 2,5 heures. Ensuite, le charbon actif imprégné est séché à la température de 100 °C à 150 °C pendant 1,0 à 6,5 heures ; par la suite, il est chauffé à la température de 180 °C à 380 °C pendant 1,5 à 2,5 heures.