RESIN COMPOSITION FOR ORGAN MODELS

[Problem] To provide a thermoplastic resin composition for organ models, which has softness more similar to those of organs, high mechanical strength and a feel similar to those of organs, also has excellent durability, and is easy to handle. [Solution] A resin composition for organ models, which contains 100 parts by mass of a component (A) that is a hydrogenated block copolymer having an MFR (as measured at a temperature of 230ºC and a load of 2.16 kg) of 1 g/10 min. or less and a component (B) that is an oil. The resin composition may additionally contain a component (C) that is a cross copolymer, a component (D) that is a polypropylene resin and a component (E) that is a filler. [Problème] Proposer une composition de résine thermoplastique pour modèles d'organes, dont la souplesse est très similaire à celle des organes, qui présente une résistance mécanique élevée et qui est semblable au toucher aux organes, qui présente également une excellente durabilité et qui est facile à manipuler. [Solution] Une composition de résine pour modèles d'organes, qui contient 100 parties en poids d'un composant (A) qui est un copolymère séquencé hydrogéné présentant un indice de fluidité à chaud (comme mesuré à une température de 230 °C et sous une charge de 2,16 kg) égal ou inférieur à 1 g/10 min et un composant (B) qui est une huile. La composition de résine peut, en outre, contenir un composant (C) qui est un copolymère réticulé, un composant (D) qui est une résine de polypropylène et un composant (E) qui est une charge. 【課題】より臓器に近い軟質性と高い力学的強度と臓器に近い感触を有し、耐久性に優れ、取り扱いが容易な臓器モデル用の熱可塑性樹脂組成物の提供。 【解決手段】成分（Ａ）としてＭＦＲ（温度２３０℃、荷重２．１６ｋｇで測定）１ｇ／１０ｍｉｎ．以下の水添ブロック共重合体１００質量部と成分（Ｂ）としてオイルを含有する臓器モデル用樹脂組成物。更に、成分（Ｃ）としてクロス共重合体、成分（Ｄ）としてポリプロピレン樹脂、成分（Ｅ）としてフィラーを含有しても良い。