HARD-COATED FILM AND METHOD FOR PRODUCING SAME

The present invention provides a hard-coated film having a hard coating layer that has good adhesion to a highly flat substrate film. This hard-coated film has a hard coating layer atop a transparent film substrate that comprises a thermoplastic acrylic resin having an arithmetic mean surface roughness (Ra) of 1 nm or less. The hard coating layer contains a curable compound having 2-5 (meth)acryloyl groups per molecule, and the content ratio of said curable compound is 25-75 wt% relative to all curable compounds in the hard coating layer. The survival rate of the hard coating layer as measured by the cross-cut method of JIS K5600 is 90% or more. La présente invention concerne un film portant un revêtement dur ayant une couche de revêtement dur qui a une bonne adhérence à un film de substrat hautement plat. Ce film portant un revêtement dur a une couche de revêtement dur au-dessus d'un substrat sous forme de film transparent qui comprend une résine acrylique thermoplastique ayant une rugosité de surface moyenne arithmétique (Ra) inférieure ou égale à 1 nm. La couche de revêtement dur contient un composé durcissable ayant 2 à 5 groupes (méth)acryloyle par molécule et la proportion dudit composé durcissable est de 25 à 75 % en poids par rapport à tous les composés durcissables présents dans la couche de revêtement dur. Le taux de conservation de la couche de revêtement dur, mesuré par la méthode de coupe transversale selon la norme JISK5600, est supérieur ou égal à 90 %. 本発明は、平坦性の高い基材フィルムとの密着性が良好なハードコート層を有するハードコートフィルムを提供する。本発明のハードコートフィルムは、算術平均表面粗さ（Ｒａ）が１ｎｍ以下の熱可塑性アクリル樹脂からなる透明フィルム基材上にハードコート層を有する。上記ハードコート層は、１分子あたり２～５個の（メタ）アクリロイル基を有する硬化性化合物を含有し、該硬化性化合物の含有割合が、上記ハードコート層中の全硬化性化合物に対して２５～７５重量％である。ＪＩＳ Ｋ５６００のクロスカット法により測定された上記ハードコート層の残存率が９０％以上である。