COMPOSITION AND METHOD FOR PRODUCING A MATTE FINISH ON THERMOFORMED ACRYLIC SHEETS

A composition for making a cast, thermoformable sheet or slab having a matte surface comprising a syrup comprising about 90% SSI - acrylic pre-polymerized syrup at 20% solids; and about 4-10% particles of about 10-15 microns in diameter of a copolymer of methyl methacrylate and ethylene glycol dimethacrylate or such particles of barium sulfate, calcium carbonate and/or silica. A method for producing a thermoformed article having a matte surface comprising mixing a syrup comprising about 90% SSI - acrylic pre-polymerized syrup at 20% solids; and about 4-10% particles of about 10-15 microns in diameter of a copolymer of methyl methacrylate and ethylene glycol dimethacrylate or such particles of barium sulfate, calcium carbonate and/or silica; heating the syrup; casting the syrup into a sheet; and thermoforming the cast sheet against a mold. L'invention concerne une composition pour fabriquer une feuille ou plaque thermoformable, coulée, ayant une surface mate, comprenant un sirop comprenant environ 90 % de sirop pré-polymérisé SSI-acrylique à 20 % de matières solides ; et environ 4-10 % de particules d'environ 10-15 microns de diamètre d'un copolymère de méthacrylate de méthyle et de diméthacrylate d'éthylène glycol ou de telles particules de sulfate de baryum, de carbonate de calcium et/ou de silice. L'invention concerne un procédé de production d'un article thermoformé ayant une surface mate comprenant le mélange d'un sirop comprenant environ 90 % de sirop pré-polymérisé SSI-acrylique à 20 % de matières solides ; et environ 4-10 % de particules d'environ 10-15 microns de diamètre d'un copolymère de méthacrylate de méthyle et de diméthacrylate d'éthylène glycol ou de telles particules de sulfate de baryum, de carbonate de calcium et/ou de silice ; le chauffage du sirop ; la coulée du sirop en une feuille ; et le thermoformage de la feuille coulée contre un moule.