SOFT THERMOPLASTIC POLYURETHANE ELASTOMERS AND PROCESS FOR THEIR PREPARATION

The present invention discloses a thermoplastic polyurethane comprising substantially no plasticizers and having a Shore A hardness of 60 or less, which is prepared by a one-step polymerization of i) linear polyol, ii) organic diisocyanate and iii) glycol chain extender mainly comprising ethylene glycol and/or 1,3-propanediol; wherein the linear polyol (i) has a number average molecular weight within the range of from 1.5 x 103 g/mol to 5.0 x 103 g/mol. The thermoplastic polyurethane of the present invention can be easily produced by conventional production methods, and the thermoplastic polyurethane thus produced can be molded to articles in practicable processing cycles. Moreover, the thermoplastic polyurethane articles have low shrinkage, have good low-temperature properties and good mechanical properties, and do not harden substantially at low temperature. La présente invention concerne un polyuréthane thermoplastique ne comprenant substantiellement pas de plastifiant et ayant une dureté Shore A de 60 ou moins, qui est préparé par une polymérisation en une étape de i) un polyol linéaire, ii) un diisocyanate organique et iii) un agent d'allongement de chaîne glycol comprenant principalement de l'éthylène glycol et/ou du 1,3-propanediol ; le polyol linéaire (i) ayant une masse moléculaire moyenne en nombre dans la plage de 1,5 x 103 g/mole à 5,0 x 103 g/mole. Le polyuréthane thermoplastique de la présente invention peut être facilement produit par des procédés de production classiques, et le polyuréthane thermoplastique ainsi produit peut être moulé en des articles dans des cycles de traitement praticables. De plus, les articles de polyuréthane thermoplastique ont un faible retrait, ont de bonnes propriétés à basse température et de bonnes propriétés mécaniques, et ne durcissent substantiellement pas à basse température.