POROUS ELECTROLYTIC POLYMER CRYOGELS FOR ENHANCED ELECTRICAL COLLAPSIBILITY

The invention provides cryogels whose porosity, pore size, pore connectivity, swelling agent concentration, and/or specific volume undergoes a change from a first value to a second value in response to an electrical stimulus. The cryogels have interconnected macropores which greatly enhance their ability to rapidly undergo volumetric collapse when subjected to moderate electric fields. The cryogels of the invention can be easily integrated into arrays capable of rapid configurational and chromatic optical modulations, and when loaded with drugs, are able to coordinate the delivery profile of multiple drugs. The cryogel can be prepared by polymerizing an aqueous solution of charged monomers and cross-linker monomers at a temperature below the freezing temperature of the solvent. L'invention concerne des cryogels dont la porosité, la taille des pores, la connectivité des pores, la concentration d'agent dilatant et/ou le volume spécifique subit/subissent un changement d'une première valeur à une seconde valeur en réponse à un stimulus électrique. Les cryogels possèdent des macropores interconnectés qui améliorent considérablement leur aptitude à subir rapidement une déformation volumétrique lorsqu'ils sont soumis à des champs électriques modérés. Les cryogels de l'invention peuvent être facilement intégrés sous forme de réseaux capables de modulations optiques configurationnelles et chromatiques rapides, et lorsqu'ils sont chargés avec des médicaments, sont aptes à coordonner le profil d'administration de médicaments multiples. Le cryogel peut être préparé par polymérisation d'une solution aqueuse de monomères chargés et de monomères réticuleurs à une température en dessous de la température de congélation du solvant.