THIN FILM COMPOSITE REVERSE OSMOSIS MEMBRANE WITH ANTIFOULING PROPERTIES AND METHOD OF PREPARATION OF THE SAME

The present invention relates to the preparation of novel antibiofouling Thin Film Composite (TFC) Reverse Osmosis (RO) membranes on porous polysulfone (PSf) support of thickness 30-40 micron. TFC-RO membranes were prepared by interfacial polymerization between neat m-phenylenediamine (MPD) in water and pyridine tricarboxylic acid chloride (PTC) or a mixture containing PTC and trimesoyl chloride (TMC) in mixture of hexane + dichloromethane. The best results in terms of flux, NaCl rejection and antibiofouling property were obtained with 2:3-1:1 weight ratio of PTC to TMC. The present invention also relates to the preparation of antibiofouling TFC membranes by the interfacial polymerization between mixture of melamine + MPD and TMC. The best results in terms of antibiofouling property, NaCl rejection and flux were obtained with 1 :1 weight ratio of MPD to melamine. La présente invention concerne la préparation de nouvelles membranes d'osmose inverse composites à film mince (TFC) anti-salissure sur un support de polysulfone poreux (PSf) d'une épaisseur de 30 à 40 microns. Les membranes TFC-RO sont préparées par polymérisation interfaciale entre du m-phénylènediamine (MPD) absolu dans de l'eau et du chlorure d'acide tricarboxylique pyridine (PTC) ou un mélange contenant du PTC et du chlorure de trimesoyl (TMC) dans un mélange d'hexane et de dichlorométhane. Les meilleurs résultats en termes de flux, de rejet de NaCl et de propriété anti-salissure ont été obtenus avec un rapport de poids 2:3-1:1 du PTC sur le TMC. La présente invention concerne également la préparation de membranes TFC anti-salissures par polymérisation interfaciale entre un mélange de mélamine et de MPD et du TMC. Les meilleurs résultats en termes de propriété anti-salissure, de rejet de NaCl et de flux ont été obtenus avec un rapport de poids 1:1 du MPD sur la mélamine..