HOT-ROLLED FERRITIC STAINLESS STEEL SHEET WITH EXCELLENT COLD CRACKING RESISTANCE AND MANUFACTURING PROCESS THEREFOR

This hot-rolled ferritic stainless steel sheet has a composition containing, in mass%, up to 0.0150 % of C, 0.01 to 2.00 % of Si, 0.01 to 2.00% of Mn, less than 0.040% of P, up to 0.010% of S, 10.0 to 30.0% of Cr, 0.001 to 0.100% of Al and up to 0.0200% of N with the balance being Fe and unavoidable impurities, and satisfies the relationship: La/L >= 0.20 [wherein L is the length of all grain boundaries with misorientation angles of 1 to less than 180° as observed in a section in the range of 1/4 to 3/4 of the sheet thickness and La is the length of subgrain boundaries with misorientation angles of 1 to less than 15° as observed therein]. L'invention concerne une feuille d'acier inoxydable férritique laminée à chaud qui a une composition contenant, en % en masse, jusqu'à 0,0150 % de C, 0,01 à 2,00 % de Si, 0,01 à 2,00 % de Mn, moins de 0,040 % de P, jusqu'à 0,010 % de S, 10,0 à 30,0 % de Cr, 0,001 à 0,100 % d'Al et jusqu'à 0,0200 % de N, le reste étant constitué de Fe et des impuretés inévitables, et qui satisfait la relation : La/L >= 0,20 [L étant la longueur de tous les joints de grains ayant des angles de désorientation de 1 à moins de 180° tels qu'observés dans une section se situant dans la plage de 1/4 à 3/4 de l'épaisseur de la feuille, et Na étant la longueur des joints de sous-grains ayant des angles de désorientation de 1 à moins de 15° tels qu'observés dans celle-ci].