METHOD FOR PRODUCING SPHEROIDAL GRAPHITE CAST IRON AND VEHICLE COMPONENT USING SAID SPHEROIDAL GRAPHITE CAST IRON

The objective of the present invention is to provide a high-performance spheroidal graphite cast iron that uses a spheroidizing agent that does not contain a rare earth element. The present invention pertains to a method for producing a spheroidal graphite cast iron having a specific final composition by performing spheroidizing processing using a spheroidizing agent that is an Fe-Si-Mg-Ca-based alloy that does not contain a rare earth element, performing inoculation processing using a first Fe-Si-based inoculation agent, and then performing molten pouring inoculation processing using a predetermined amount of a second Fe-Si-based inoculation agent containing 45-75% of Si, 1-3% of Ca, and no greater than 15 ppm of Ba. La présente invention a pour but de proposer une fonte à graphite sphéroïdal à haute performance qui utilise un agent de sphéroïdisation qui ne contient pas d'élément des terres rares. La présente invention porte sur un procédé de fabrication d'une fonte à graphite sphéroïdal ayant une composition finale spécifique par réalisation d'un traitement de sphéroïdisation à l'aide d'un agent de sphéroïdisation qui est un alliage à base de Fe-Si-Mg-Ca qui ne contient pas d'élément des terres rares, réalisation d'un traitement d'inoculation à l'aide d'un premier agent d'inoculation à base de Fe-Si, puis réalisation d'un traitement d'inoculation lors de la coulée à l'état fondu à l'aide d'une quantité prédéterminée d'un second agent d'inoculation à base de Fe-Si contenant 45-75 % de Si, 1-3 % de Ca et pas plus de 15 ppm de Ba.