GLASS COMPOSITION SUITABLE FOR CHEMICAL STRENGTHENING AND CHEMICALLY STRENGTHENED GLASS ARTICLE

A glass composition that has a high heat resistance, is suitable for chemical strengthening, and is suitable for use in a large-scale facility for the mass production of glass plates by the float glass process, and the like, is a glass composition comprising, by mass%, 60 to 66% of SiO2, 10 to 16% of Al2O3, 0 to 1% of B2O3, 3 to 10% of MgO, 0 to 1% of CaO, 1 to 9% of SrO, 0 to 4% of BaO, 0 to 2% of ZnO, 0 to 1% of Li2O, 10 to 20% of Na2O, 0 to 5% of K2O, 0 to 2% of TiO2, and 0 to 0.1% of ZrO2, wherein MgO + CaO + SrO + BaO is within a range of 10 to 20%, Li2O + Na2O + K2O is within a range of 14 to 20%, and the Sr content is greater than the CaO content. La présente invention concerne une composition de verre ayant une forte résistance à la chaleur, convenant au renforcement chimique et convenant à une utilisation dans une installation à grande échelle pour la production en masse de plaques de verre par le procédé du verre flotté, et similaire, étant une composition de verre comprenant, en pourcentages en poids, 60 à 66% de SiO2, 10 à 16% de Al2O3, 0 à 1% de B2O3, 3 à 10% de MgO, 0 à 1% de CaO, 1 à 9% de SrO, 0 à 4% de BaO, 0 à 2% de ZnO, 0 à 1% de Li2O, 10 à 20% de Na2O, 0 à 5% de K2O, 0 à 2% de TiO2, et 0 à 0,1% de ZrO2, où MgO + CaO + SrO + BaO est contenu entre 10 et 20%, Li2O + Na2O + K2O est contenu entre 14 et 20%, et où la teneur en Sr est supérieure à la teneur en CaO.