METHOD FOR PREPARING POLYCRYSTALLINE ALUMINUM OXYNITRIDE HAVING ENHANCED TRANSPARENCY

The present invention relates to a method for preparing polycrystalline aluminum oxynitride having enhanced transparency, and more particularly, to a method for preparing polycrystalline aluminum oxynitride by sintering a powder mixture of Al2O3 and AlN under atmospheric pressure, wherein the content of AlN is set to 17 to 26 mol %, a first sintering is performed at 1,575°C to 1,675°C so as to enable raw-material powders to have a relative density of 95% or higher, and a second sintering is performed so as to enable the raw-material powders to have a higher relative density. According to the present invention, all internal micropores are removed, and thus cubic polycrystalline aluminum oxynitride ceramic having a visible-light transmittance of 70% or higher can be obtained in a short amount of time at a relatively low sintering temperature. La présente invention concerne un procédé de préparation d'oxynitrure d'aluminium polycristallin ayant une transparence améliorée, et plus particulièrement un procédé de préparation d'oxynitrure d'aluminium polycristallin par frittage d'un mélange de poudre d'Al2O3 et d'AlN sous pression atmosphérique, dans lequel la teneur en AlN est ajustée entre 17 et 26 % en mole, un premier frittage est effectué entre 1 575 °C et 1 675 °C de façon à permettre aux poudres de matières premières d'avoir une densité relative supérieure ou égale à 95 %, et un second frittage est effectué de façon à permettre aux poudres de matières premières d'avoir une densité relative plus élevée. Selon la présente invention, tous les micropores internes sont retirés et ainsi une céramique d'oxynitrure d'aluminium polycristallin cubique ayant une transmittance de la lumière visible supérieure ou égale à 70 % peut être obtenue en une courte durée à une température de frittage relativement basse.