FLAME RETARDANT, OPTICALLY CLEAR THERMOPLASTIC MOLDING COMPOSITION

The present invention relates to a flame-retardant, optically clear thermoplastic molding composition. The composition contains a A) about 60 pbw to about 97 pbw of a polycarbonate, B) about 1 pbw to about 20 pbw of bromine- substituted oligocarbonate, C) about 1 pbw to about 20 pbw of a phosphorus- containing compound and D) about 0.01 pbw to about 1 pbw of at least one alkali or alkaline- earth salt of perfluoroalkane sulfonic acid and optionally E) about 0.01 to about 1 pbw of a phosphite antioxidant/stabilizer. In accordance with UL-94 standard the flame-retardant, optically clear thermoplastic molding composition is rated 5VA at 3.00 mm and V-O at 2.3 mm, more preferably V-O at 1.5 mm according to UL-94. La présente invention concerne une composition de moulage thermoplastique optiquement transparente et ignifuge. La composition contient A) environ 60 parties en poids à environ 97 parties en poids d'un polycarbonate, B) environ 1 partie en poids à environ 20 parties en poids d'un oligocarbonate à substitution brome, C) environ 1 partie en poids à environ 20 parties en poids d'un composé contenant du phosphore et D) environ 0,01 partie en poids à environ 1 partie en poids d'au moins un sel alcalin ou alcalinoterreux d'acide perfluoroalcane sulfonique et facultativement E) environ 0,01 à environ 1 partie en poids d'un antioxydant/stabilisant à base de phosphite. Conformément à la norme UL-94, la composition de moulage thermoplastique optiquement transparente et ignifuge est classée 5 VA à 3,00 mm et V0 à 2,3 mm, de préférence encore V0 à 1,5 mm d'après la norme UL-94.