METHOD OF MAKING AND USE OF MOLECULAR SIEVE OF MFS FRAMEWORK TYPE WITH CONTROLLABLE AVERAGE SIZE

A method of making a crystalline molecular sieve of MFS framework type, preferably ZSM-57, from a synthesis mixture comprising at least one source of tetravalent element (Y), at least one source of trivalent element (X), at least one source of alkali metal hydroxide (MOH), at least one structure-directing-agent (R) and water, said alkali metal (M) comprising potassium, and having the following mole composition (expressed in terms of oxide): YO2:(P) X2O3:(q)OH-:(r)R:(s)H2O, wherein (p) is in the range from 0.005 to 0.05, (q) is in the range from 0.01 to 3, (r) is in the range from 0.03 to 2 and (s) is in the range from 10 to 75 (based on total weight of said synthesis mixture); wherein the crystals of molecular sieve formed having an average diameter (D) of less than or equal to 1.5 micron and an average thickness (T) of less than or equal to 300 nanometers. L'invention porte sur un procédé de fabrication d'un tamis moléculaire cristallin du type à structure MFS, de préférence ZSM-57, à partir d'un mélange de synthèse comprenant au moins une source d'élément tétravalent (Y), au moins une source d'élément trivalent (X), au moins une source d'hydroxyde de métal alcalin (MOH), au moins un agent structurant (R) et de l'eau, ledit métal alcalin (M) comprenant du potassium, et ayant la composition molaire suivante (exprimée en termes d'oxyde) : YO2:(p) X2O3:(q)OH-:(r)R:(s)H2O, dans laquelle (p) est dans l'intervalle de 0,005 à 0,05, (q) est dans l'intervalle de 0,01 à 3, (r) est dans l'intervalle de 0,03 à 2 et (s) est dans l'intervalle de 10 à 75 (sur la base du poids total dudit mélange de synthèse); les cristaux de tamis moléculaire formés ayant un diamètre moyen (D) inférieur ou égal à 1,5 micromètres et une épaisseur moyenne (T) inférieure ou égale à 300 nanomètres.