RUBBER COMPOSITION FOR RECOVERING MOLD RELEASABILITY

A rubber composition for recovering releasability from compression molds. The composition is used to impart releasing properties to a mold surface after a fouling substance resulting from the step of molding a curable resin has been removed from the mold surface. The composition contains, as a base resin, an unvulcanized rubber comprising an ethylene/propylene rubber and a butadiene rubber in a proportion of from 90/10 to 50/50 by parts by weight, and contains a specific release agent. The unvulcanized rubber is an unvulcanized rubber which, after having been vulcanized and cured, has an elongation of 80-800%, a tensile strength of 3-10 MPa, and a rubber hardness (durometer hardness) of A60 to A95, and which has a 90% vulcanization time as measured at a mold temperature of 175° (proper vulcanization point), tc(90), in the range of 50-100 sec or 200-400 sec. La présente invention concerne une composition permettant de rétablir l'aptitude au démoulage de moules de compression. La composition sert à conférer à une surface de moule des propriétés d'aptitude au démoulage après qu'on ait éliminé de cette surface du moule une substance d'encrassement résultant de l'opération de moulage d'une résine durcissable. La composition contient, d'une part une résine de base constitué d'un caoutchouc non vulcanisé contenant un caoutchouc à l'éthylène/propylène et un caoutchouc au butadiène dans des proportions allant de 90/10 à 50/50 par parties en poids, et d'autre part un agent de démoulage spécifique. Le caoutchouc non vulcanisé est d'un type qui, une fois durci et vulcanisé, présente un coefficient d'élongation de 80-800%, une résistance à la traction de 3-10 MPa, et une dureté de gomme (dureté au duromètre) de A60 à A95, et dont le temps de vulcanisation à 90% "tc(90)" se situe dans une plage de 50 à 100 secondes ou de 200 à 400 secondes pour une température de 175° (température de vulcanisation propre).