LITHIUM SECONDARY BATTERY ANODE SUBSTANCE AND METHOD FOR MANUFACTURING

Manufactured is a lithium secondary battery anode active substance composed of a petroleum-based heavy oil and a carbon material using at least one petroleum-based heavy oil as starting material. For said active substance, interval d002 of the crystal plane measured by X-ray diffraction is 0.340 nm or larger. The crystallite size Lc (110) in the direction of the C axis is 10 nm or smaller. The intensity ratio (R = I1360/I1580) of the diffraction peak near 1360 cm-1 to the diffraction peak near 1580 cm-1 measured by the Raman spectral method is in the range of 0.8-1.2. The total porosity volume on the surface is 0.02 cc/g or higher. The volume of pores of 10 nm or smaller is in the range of 0.01-0.1 cc/g, and the pore area is 50 m2/g or larger. La présente invention concerne la fabrication d'une substance active anodique de pile secondaire au lithium composée d'une huile lourde à base de pétrole et d'un matériau carboné utilisant au moins une huile lourde à base de pétrole comme matériau de départ. Pour ladite substance active, un intervalle d002 du plan cristallin mesuré par une diffraction aux rayons X est de 0,340 nm ou plus. La taille de la cristallite Lc (110) dans le sens de l'axe des C est de 10 nm ou moins. Le rapport d'intensité (R = I1360/I1580) du pic de diffraction près de 1 360 cm-1 au pic de diffraction près de 1 580 cm-1 mesurés par le procédé du spectre Raman se situe dans la plage de 0,8 à 1,2. Le volume de porosité total sur la surface est de 0,02 cm3/g ou plus. Le volume des pores de 10 nm ou moins se situe dans la plage de 0,01 à 0,1 cm3/g et la surface des pores est de 50 m2/g ou plus.