HIGH CARBON SURFACE DENSIFIED SINTERED STEEL PRODUCTS AND METHOD OF PRODUCTION THEREFOR

A powder mixture alloy is provided for manufacturing surface densified high carbon sintered steel articles containing iron or iron pre-alloyed powder, which has been preliminary mixed with at least 0.4 wt% graphite, lubricant and optionally at least one alloying element from the group of nickel, chromium, copper, manganese and molybdenum. Components are manufactured utilizing the alloy mixture comprising the steps of: a) compacting the metallic powder to obtain a compact; b) pre- sintering the compact at a low temperature to prevent graphite from diffusing into the iron; c) surface densifying of the pre-sintered compact to a predetermined densification depth; d) sintering under neutral gas or carburizing atmosphere; e) heat treating the sintered compact. La présente invention concerne un alliage de mélange de poudres pour fabriquer des articles à base d'acier à forte teneur en carbone fritté contenant du fer ou de la poudre fer préalliée, qui a été préalablement mélangée avec au moins 0,4% en poids de graphite, un lubrifiant et éventuellement au moins un élément d'alliage choisi parmi le groupe constitué de nickel, de chrome, de cuivre, de manganèse et de molybdène. L'invention concerne également la fabrication de composants au moyen du mélange d'alliage comprenant les étapes suivantes : a) la compression de la poudre métallique pour obtenir un comprimé; b) le frittage préalable du comprimé à basse température pour empêcher la diffusion du graphite dans le fer; c) la densification de surface du comprimé préalablement fritté jusqu'à une profondeur de densification prédéterminée; d) le frittage sous un gaz neutre ou une atmosphère de cémentation; e) le traitement thermique du comprimé fritté.