CATALYST AND HYDROTREATING PROCESS

A process for the preparation of a catalyst, which process comprises the steps of : i) mixing an alumina precursor with combustible carbon-containing fibres with a diameter in the range of from 0.5 to 5 microm. and a length of no greater than 100 microm. in an amount in the range of from 20 to 40 wat % based on the total dry mixture; ii) adding nitric acid and water to form an extrudable mass; iii) extruding the mixture to form shaped particles; iv) drying the shaped particles; v) heating the particles in an atmosphere comprising no more than 5 vol % oxygen at a temperature in the range of from 350 to 600 °C; and vi) then heating the particles in a gas mixture comprising at least 12 vol % oxygen at a temperature in the range of from 450 to 600 °C. A catalyst obtainable by said process, and process for the demetallisation of hydrocarbon fraction with said catalyst. L'invention concerne un procédé de préparation d'un catalyseur, dont le procédé comprend les étapes consistant: i) à mélanger un précurseur d'alumine avec des fibres contenant du carbone combustible à diamètre compris entre 0,5 et 5 micromètres et une longueur inférieure ou égale à 100 micromètres dans une quantité comprise entre 20 et 40 % en poids sur la base du mélange sec total; ii) à ajouter un acide nitrique et de l'eau afin de former une masse extrudable; iii) à extruder le mélange afin de former des particules façonnées; iv) à sécher les particuliers façonnées; v) à chauffer ces particules dans une atmosphère comprenant pas plus de 5 volumes % d'oxygène à une température comprise entre 350 et 600 °C; et vi) à chauffer ensuite les particules dans un mélange gazeux contenant au moins 12 volumes % d'oxygène à une température comprise entre 450 et 600 °C. L'invention concerne également un catalyseur pouvant être obtenu au moyen de ce procédé, et un procédé destiné à démétalliser une fraction d'hydrocarbone au moyen de ce catalyseur.