ALUMINIUM-BASED POWDER COMPOSITE MIXTURE AND METHOD FOR THE PRODUCTION THEREOF

The invention relates to powder metallurgy. The inventive aluminium-based powder composite mixture comprises components with the following component ratio: 41-43 mass % silicon, 4,1-5.2 mass % nickel, 0.05-0.1 mass % phosphorus and 0.01-0.05 mass % aluminium nitride, the rest being aluminium. The inventive method for producing said powder composite mixture consists in preparing a melt containing aluminium, silicon and nickel and, subsequently, in pulverising said melt by nitrogen at a temperature and pressure which enable the aluminium nitride to be formed. Said invention makes it possible to obtain a construction material which exhibits a high operating performance, a high operational reliability for a long service life, is non-toxic and inexpensive. The thus obtainable material can be used for accurate engineering products, in particular for aircraft instruments. L'invention appartient au domaine de la métallurgie des poudres. Le mélange de poudres composite comprend les composants suivants, en % de poids: silicium 41 ÷ 43, nickel 41 ÷ 52, phosphore 0,05 ÷ 0,1; nitrure d'aluminium 0,01 ÷ 0,05, le reste étant de l'aluminium. Le procédé de fabrication du mélange de poudres composite consiste en ce qui suit: préparer un bain de fusion contenant de l'aluminium, du silicium, du nickel et du phosphore; et à pulvériser ce bain de fusion avec de l'azote à une pression et une température assurant la formation du nitrure d'aluminium. L'invention permet de fabriquer un matériau possédant des caractéristiques fonctionnelles et une fiabilité d'usage élevées pendant une durée de service prolongée et étant peut cher et non toxique. Le matériau ainsi obtenu peut s'utiliser dans des articles de constructions mécaniques de précision et notamment dans la création d'instruments pour aéronefs.