THERMOPLASTIC OLEFIN COMPOSITIONS AND INJECTION MOLDED ARTICLES MADE THEREOF

A thermoplastic polymer composition that exhibits substantially isotropic post injection molding shrinkage. The thermoplastic polymer composition includes a blend of highly crystalline polypropylene homopolymer, an ethylene-C4-8 a-olefin plastomer and talc having a D50 of about 2.0 µm or less. The thermoplastic polymer composition exhibits post injection molding shrinkage, low temperature impact strength and tensile strength that is similar to or better than relatively expensive engineering resins and blends. The thermoplastic polymer composition according to the invention is particularly useful for forming injection molded parts for motor vehicles. L'invention concerne un composition polymère thermoplastique présentant un retrait après moulage par injection sensiblement isotrope. Cette composition polymère thermoplastique comprend un mélange d'un homopolymère de propylène hautement cristallin, d'un plastomère a-oléfinique d'éthylène C4-8 et d'un talc présentant une valeur D50 inférieure ou égale à environ 2,0 µm. Ladite composition polymère thermoplastique présente un retrait après moulage par injection, une résistance au choc à basse température et une résistance à la traction similaires ou supérieurs à ceux des mélanges et des résines techniques de coût relativement élevé. La composition polymère thermoplastique de l'invention est particulièrement utile pour former des pièces moulées par injection pour véhicules à moteur.