DYE MATERIALS AND INFRA RED ACTIVE POLYMER COMPOSITIONS THEREOF

Nanopigments were prepared from organic IR dye and Na-bentonite with CEC of 95 mmole Na per 100 g of bentonite, at room temperature, by dissolving the Na-bentonite in water and mixing for 2 hours, and mixing in the dye, dissolved in ethanol, for 18 hours. The precipitate is filtered, washed three times with water/ethanol mixture, dried at 105 °C for 10 hours, and milled in a kitchen miller for 2 mins. 0.3 parts of the nanopigments were mixed to 100 parts of pulverized SPG resin and processed in an extruder with a die temperature of 190 °C to form transparent, faintly green or grey coloured extrudates which were used to press film of 0.4 mm thickness at 160 °C. The films were used to prepare IR-active laminated glass. Near infrared absorption spectra of the glass structures were obtained in a Perkin-Elmer Spectrophotometer. Selon cette invention, on a préparé des maillots pigments à partir d'un colorant infrarouge organique et de bentonite de sodium ayant une capacité d'échange cationique (CEC) de 95 mmole Na par 100 g de bentonite, à température ambiante, en dissolvant la bentonite de sodium dans l'eau et en la mélangeant pendant deux heures, puis en la mélangeant dans le colorant, dissous dans l'éthanol, pendant 18 heures. Le précipitat est ensuite filtré, lavé trois fois avec un mélange eau/éthanol, séché à 105 °C pendant 10 heures est passé ou broyé heures pendant deux minutes. 0,3 parties des nanopigments ont été mélangées à 100 parties de la résine SPG, pulvérisées et traitées dans une extrudeuse à température de traitement de 190 °C de façon à obtenir des extrudats transparents, légèrement colorés, verts ou gris, qui ont été utilisés pour comprimer le film d'une épaisseur de 0,4 mm à 160 °C. Les films ont été utilisés pour préparer un verre laminé actif infrarouge. Les spectres d'absorption du proche infrarouge des structures de verre ont été obtenus dans un spectrophotomètre de Perkin-Elmer.