Method of manufacturing ultra low carbon ferritic stainless steel

A method of manufacturing a ferritic stainless steel containing an ultra low level of carbon concentration in molten steel within time shorter than existing technology by controlling content, appropriate composition, and liquid-state fraction, etc., of Cr2 O3 in slag to maximize vacuum decarburization refining efficiency, the method comprising: tapping molten steel to a ladle in a non-deoxidized state after pre-decarburization and denitrification in an ARGON OXYGEN DECARBURIZATION refining furnace and then removing non-deoxidized slag; placing the ladle in a vacuum furnace, reducing pressure and then blowing-in oxygen gas from the upper of the molten steel through a lance; creating Al2 O3 by injecting Al at point of time of beginning of oxygen blowing; forming CaO-Al2 O3 -Cr2 O3 -MgO-based slag by injecting calcium oxide at point of time of completion of the oxygen blowing; and supplying inert gas through a porous plug on a bottom of the ladle.