Process for in-situ etching a hardmask stack

A method of etching high aspect ratio, anisotropic deep trench openings in a silicon substrate coated with a multilayer mask comprising in sequence a pad oxide layer, a silicon nitride layer, a doped or undoped silicon oxide hard mask layer, a polysilicon hard mask layer, an antireflection coating and a patterned photoresist layer in a single chamber comprising patterning the antireflection coating and hard mask layer, removing the photoresist and antireflection layers with oxygen, using the patterned polysilicon as a hard mask layer etching an opening in the silicon oxide hard mask layer, the silicon nitride layer and the pad oxide layer, removing the polysilicon hard mask layer with CF4/CHF3, and etching an anisotropic deep trench in the silicon substrate using the patterned silicon oxide hard mask layer as a mask and an etchant mixture including nitrogen trifluoride that self-cleans the chamber.