GLASS COMPOSITION FOR CHEMICAL STRENGTHENING AND CHEMICALLY STRENGTHENED GLASS ARTICLE

The present disclosure provides a glass composition which is for chemical strengthening, from which a glass sheet can be produced by a common float process, and which is suitable for achieving both a surface compressive stress and a compressive stress layer depth. The glass composition according to the present disclosure includes, as components, in mol %: 60 to 80% SiO2; 1 to 5% Al2O3; 5 to 25% MgO; 0 to 5% CaO; 10 to 20% Na2O; and 0 to 10% K2O. A chemically strengthened glass article, for example, having a surface compressive stress of 500 MPa or more and a compressive stress layer depth of 10 μm or more can be provided using the glass composition.