STEEL FOR NITRIDING AND NITRIDED COMPONENT

A nitrided component has a chemical composition consisting of, by mass percent, C: 0.07-0.14%, Si: 0.10-0.30%, Mn: 0.4-1.0%, S: 0.005-0.030%, Cr: 1.0-1.5%, Mo: ≦0.05% (including 0%), Al: 0.010% or more to less than 0.10%, V: 0.10-0.25%, optionally at least one element selected from Cu: ≦0.30% and Ni...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	YUYA Masato, IMATAKA Hideki, GYOTOKU Yuya, KOBAYASHI Atsushi, MAEDA Susumu
Format:	Patent
Sprache:	eng
Schlagworte:	ALLOYS CHEMICAL SURFACE TREATMENT CHEMISTRY COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATIONOR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY IONIMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL COATING MATERIAL WITH METALLIC MATERIAL COATING METALLIC MATERIAL DIFFUSION TREATMENT OF METALLIC MATERIAL FERROUS OR NON-FERROUS ALLOYS GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION INGENERAL MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS METALLURGY METALLURGY OF IRON MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THESURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION TREATMENT OF ALLOYS OR NON-FERROUS METALS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	A nitrided component has a chemical composition consisting of, by mass percent, C: 0.07-0.14%, Si: 0.10-0.30%, Mn: 0.4-1.0%, S: 0.005-0.030%, Cr: 1.0-1.5%, Mo: ≦0.05% (including 0%), Al: 0.010% or more to less than 0.10%, V: 0.10-0.25%, optionally at least one element selected from Cu: ≦0.30% and Ni: ≦0.25%, [0.61Mn+1.11Cr+0.35Mo+0.47V≦2.30], and the balance of Fe and impurities. P, N, Ti and O among the impurities are P: ≦0.030%, N: ≦0.008%, Ti: ≦0.005%, and O: ≦0.0030%. The nitrided composition is suitable for use as an automobile ring gear. The nitrided component has a surface hardness of 650-900 HV, core hardness being ≧150 HV, effective case depth of ≧0.15 mm, has excellent bending fatigue strength and surface fatigue strength although the content of Mo is as low as ≦0.05% and has a small amount of expansion caused by nitriding.