Method for producing spherical aluminum nitride power

The present invention provides method for producing a spherical aluminum nitride powder. In an embodiment, the method comprises mixing an Al precursor and a flux in a solvent to produce a mixed solution, spray-drying the mixed solution to form a spray-dried powder, mixing the spray-dried powder and a carbon-based material to form a mixture, heat treating the mixture in a nitrogen atmosphere to form a heat-treated compound, and decarbonizing the heat-treated compound in an air atmosphere, wherein the flux is at least one selected from the group consisting of Cu2O, TiO2, Bi2O3, and CuO, or a mixture of at least one selected from the group consisting of Cu2O, TiO2, Bi2O3, and CuO and at least one selected from the group consisting of CaF2 and Y2O3.