Method of producing roughly shaped material for rolling bearing

A roughly shaped material for a rolling bearing of the present invention is produced by forging a steel composed of a high-carbon chrome bearing steel containing 0.7 mass % to 1.2 mass % of a carbon, and 0.8 mass % to 1.8 mass % of a chromium to a predetermined shape while heating the steel to a for...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	Neishi, Yutaka, Saitou, Toshikazu, Kashiwagi, Shinichirou, Hirano, Tetsurou, Yano, Takefumi, Uekita, Hiroki
Format:	Patent
Sprache:	eng
Schlagworte:	ALLOYS BEARINGS BLASTING CHEMISTRY ELEMENTS OR CRANKSHAFT MECHANISMS ENGINEERING ELEMENTS AND UNITS FERROUS OR NON-FERROUS ALLOYS FLEXIBLE SHAFTS GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVEFUNCTIONING OF MACHINES OR INSTALLATIONS HEATING LIGHTING MAKING FORGED OR PRESSED METAL PRODUCTS, e.g. HORSE-SHOES,RIVETS, BOLTS OR WHEELS MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS MECHANICAL ENGINEERING MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL METALLURGY METALLURGY OF IRON MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS PERFORMING OPERATIONS PUNCHING METAL ROTARY BODIES OTHER THAN GEARING ELEMENTS SHAFTS THERMAL INSULATION IN GENERAL TRANSPORTING TREATMENT OF ALLOYS OR NON-FERROUS METALS WEAPONS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	A roughly shaped material for a rolling bearing of the present invention is produced by forging a steel composed of a high-carbon chrome bearing steel containing 0.7 mass % to 1.2 mass % of a carbon, and 0.8 mass % to 1.8 mass % of a chromium to a predetermined shape while heating the steel to a forging temperature in a range of (Ae1 point+25° C.) to (Ae1 point+105° C.), cooling a forged article to a temperature of Ae1 point or lower, and performing an annealing in which the forged article that is obtained is heated to a soaking temperature in a range of (Ae1 point+25° C.) to (Ae1 point+85° C.), the forged article is retained for 0.5 hours or longer, and the forged article is cooled down to 700° C. or lower at a cooling rate of 0.30° C./s or slower.