EXTRA-RAPID CURING STEAMING-FREE CONCRETE

The invention relates to structural concretes, in particular to extra-rapid curing ones, and can be used with highest effectiveness at production of reinforced-concrete ties. The especially quickly curing concrete consists of ballast, sand, cement, water, superplasticizer admixture C-3 (or its analog) and addition-electrolyte, and as an electrolyte admixture one uses calcium chloride CaCl, content of admixture C-3 (or its analog) and CaCl, ballast, sand, cement and water is taken as optimal, B, S, Cand W, (C-3)and (CaCl), at that optimal amount of admixture C-3 (or its analog) is determined by the curve of dependence of conventional viscosity of vibrated cement-water mix with W/C=0.23 on content of addition, this varies within 0 % and 1,0 % in 0,1 %, optimum consumptions of ballast, sand, cement and water are determined by formulas. Optimum amount of admixture CaClis determined by maximum strength of concrete samples with optimum consumptions of B, S, Cand W, (C-3)in 12 hours of curing at a temperature of 30 °C, at preparation of concrete mixture the admixture CaClis added at the end of mixing, one controls free laying of concrete mixture by characteristics of setting the cone OK≤2 cm and vibratory solubility VS≤120 s, and after formation concrete is cured in the form in steaming chamber without steam supply at a temperature not less than 30 °C, or in summer at same temperature at open site during 12-18 hours. The object of the invention is in producing extra-rapid curing concrete with strength higher than 32 MPa in 12 hours of steaming-free curing, suitable for pre-stressed reinforced-concrete ties, at minimum required (optimum) consumption of superplasticizer admixture C-3. Винахід належить до конструктивних бетонів, зокрема особливошвидкотверднучих, і може бути найефективніше використаний при виробництві залізобетонних шпал.Особливошвидкотверднучий безпропарювальний бетон складається з щебеню, піску, цементу, води, добавки-суперпластифікатора С-3 (або її аналога) і добавки-електроліту, та як добавка-електроліт використовується хлористий кальцій СаСl, вміст добавок С-3 (або її аналога) і СаСl, щебеню, піску, цементу і води приймають оптимальними, відповідно, Щ, П, Ці В, (С-3)і (СаСl), при цьому оптимальна кількість добавки С-3 (або її аналога) визначається по кривій залежності умовної в'язкості віброваної цементно-водної суміші з В/Ц=0,23 від вмісту добавки, що змінюється в межах від 0 % до 1,0 % через 0,1 %, оптимальні витрати щебеню, піску, цементу і в