steel-making rolled products for PRODUCTION metal goods of increased strength

Steel-making rolled products for production metal goods of increased strength from low carbon steel of smooth round profile is made as a core with the diameter between 6.0 and 22.0 mm, formed in the coil. The rolled products have a flow limit not less than 350 N/mm2, rupture strength of at least 480 N/mm2, percentage of elongation ((5) at least 30 %, relative narrowing of at least 60 % and it is made from steel containing 0.14 ... 0.30 % carbon, 0.6 ... 1.6 % manganese, 0.015 ... 0.030 % nitrogen, 0.025 ... 0.070 % aluminum, 0.005 ... 0.040 % titanium, the rest is iron and unavoidable impurities. Прокат передельный для производства метизной продукции повышенной прочности из низкоуглеродистой стали гладкого круглого профиля выполнен в виде стержня диаметром от 6,0 до 22,0 мм, сформированного в моток. Прокат имеет предел текучести не менее 350 Н/ мм2, временное сопротивление разрыва не менее 480 Н/ мм2, относительное удлинение ((5) не менее 30 %, относительное сужение не менее 60 % и изготовлен из стали, содержащей 0,14 ... 0, 30 % углерода, 0,6 ... 1,6 % марганца, 0,015 ... 0,030 % азота, 0,025 ... 0,070 % алюминия, 0,005 ... 0,040 % титана, остальное железо и неизбежные примеси. Прокат передільний для виробництва метизної продукції підвищеної міцності з низьковуглецевої сталі гладкого круглого профілю виконаний у вигляді стрижня діаметром від 6,0 до 22,0 мм, сформованого в моток. Прокат має межу плинності не менше 350 Н/мм2, тимчасовий опір розриву не менше 480 Н/мм2, відносне подовження ((5) не менше 30 %, відносне звуження не менше 60 % і виготовлений із сталі, що містить 0,14...0,30 % вуглецю, 0,6...1,6 % марганцю, 0,015...0,030 % азоту, 0,025...0,070 % алюмінію, 0,005...0,040 % титану, решта залізо і неминучі домішки.