METHOD OF OUT-OF-FURNACE TREATMENT OF CAST IRON BY INJECTION OF DISPERSED MAGNESIUM

The invention relates to ferrous metallurgy. A method of out-of-furnace treatment of cast iron, which includes blowing dispersed magnesium into the melt volume in a gas-powder jet through at least one nozzle of a rotating submerged tuyere, wherein the dispersed magnesium is blown in with particles of 0.2-1.6 mm to a depth of 0.5-4.5 m, at a concentration of magnesium in the gas carrier of 6-50 kg/m3, with a gas-powder jet velocity at the tuyere cut of 70-110 m/s and a rotation period of the single-nozzle tuyere Tod.= 1.5-6.7 s, which is equal to the duration of bubbles floating in the melt of a mixture of magnesium vapor and gas carrier. Technical result: ensuring a stable technological (without splashes) injection of dispersed magnesium, reducing the processing cycle, increasing the efficiency of magnesium use, increasing the reliability and durability of equipment, improving the quality of cast iron. Винахід належить до чорної металургії. Спосіб позапічної обробки чавуну, який включає вдування в об'єм розплаву диспергованого магнію в газопорошковому струмені через щонайменше одне сопло зануреної фурми, яка обертається, причому диспергований магній вдувають з частинками 0,2-1,6 мм на глибину 0,5-4,5 м, при концентрації магнію в газоносії 6-50 кг/м3, зі швидкістю газопорошкового струменя на зрізі фурми 70-110 м/с і періодом обертання односоплової фурми Тод.=1,5-6,7 с, який дорівнює тривалості спливання в розплаві бульбашок суміші пари магнію з газоносієм. Технічний результат: забезпечення стійкого технологічного (без виплесків) введення диспергованого магнію, скорочення циклу обробки, підвищення ефективності використання магнію, підвищення надійності і довговічності роботи обладнання, поліпшення якості чавуну.