A METHOD FOR PRODUCING FINELY DISPERSED METAL CARBIDES

The invention relates to powder metallurgy. According to the method for producing fine metal carbides, the electric discharge chamber is filled with hydrocarbon liquid, metal powder is loaded in a ratio of solid to liquid phases from 1:3 to 1:30, a high voltage is applied to the electrodes, and high-voltage pulse discharges are applied with a voltage of 50 kV, a current growth rate of 6 GA/s and a specific energy of 2.5 to 20 MJ/kg. The electrodes used are a multi-structured anode, which is preliminarily immersed in metal powder to a depth of 3 to 5 mm, and a cathode, which is the bottom of the electro-discharge chamber. The invention reduces the amount of residual free carbon and increases the amount of fine metal carbides formed. Винахід належить до порошкової металургії. Відповідно до способу одержання тонкодисперсних карбідів металів електророзрядну камеру заповнюють вуглеводневою рідиною, завантажують металевий порошок у співвідношенні твердої і рідкої фаз від 1:3 до 1:30, подають на електроди високу напругу та здійснюють дію високовольтними імпульсними розрядами з напругою 50 кВ, швидкістю зростання струму 6 ГА/с та з питомою енергією від 2,5 до 20 МДж/кг. Як електроди використовують багатовістрійний анод, який попередньо занурюють у металевий порошок на глибину від 3 до 5 мм, та катод, яким є днище електророзрядної камери. Винахід забезпечує зменшення кількості залишкового вільного вуглецю та збільшення кількості утворених тонкодисперсних карбідів металів.