METHOD For STEEL REFINING

The invention relates to ferrous metallurgy. A method for steel refining includes supplying a portion of the liquid slag in the casting ladle from the steelmaking aggregate, then adding the deoxidizing agent and metal tapping after aging at least 1 minute, at that when the ladle is filled to 1/4-1/3 of its height the addition of portion of solid slag-forming mixture is started, which mixture is composed of lime and fluorspar with the ratio of components of CaO : CaF2 = (3-4): 1. The technical result is in decrease in amount of harmful impurities in the steel (sulfur approximately by 25 %, phosphorus by 10 %), the reduction in internal and external defects in the molded workpiece by 1.5 times. Изобретение относится к черной металлургии. Способ рафинирования стали включает подачу в сталеразливочный ковш из сталеплавильного агрегата порции жидкого шлака, затем добавление раскислителя и после выдержки не менее 1 минуты выпуск металла, причем при наполнении ковша на 1/4-1/3 его высоты начинают присадку порции твердой шлакообразующей смеси извести и плавикового шпата с соотношением компонентов СаО : CaF2 = (3-4) : 1. Технический результат: уменьшение содержания вредных примесей в стали: серы примерно на 25 % и фосфора - на 10 %, снижение внутренних и внешних дефектов литой заготовки в 1,5 раза. Винахід належить до чорної металургії. Спосіб рафінування сталі включає подачу в сталерозливний ківш із сталеплавильного агрегату порції рідкого шлаку, потім додавання розкислювача і після витримки не менше 1 хвилини випуск металу, причому при наповненні ковша на 1/4-1/3 його висоти починають присадку порції твердої шлакоутворюючої суміші з вапна і плавикового шпату із співвідношенням компонентів СаО:CaF2=(3-4):1. Технічний результат: зменшення вмісту шкідливих домішок в сталі: сірки приблизно на 25 % та фосфору - на 10 %, зниження внутрішніх і зовнішніх дефектів литої заготівки в 1,5 разу.