METHOD OF PRODUCING BORIC ACID

FIELD: production of inorganic compounds. SUBSTANCE: invention relates to production of boric acid by sulfuric acid method from boron-silicate material with iron content more than 2%. Datolite concentrate containing 2.0-5.5% of ferric oxide is mixed with recycled solutions and sulfuric acid. After slurry has been agitated and aged at 105-107 C for 90 min, recycled solutions are added and slurry is neutralized by calcined datolite ore and calcium borate. Slurry is then leached at 65 C for 45 min and filtered to yield production solution and slime. The latter is washed with water and simultaneously treated with carbon dioxide-containing gas to pH 6.15-6.40 whereupon obtained slurry is filtered out. Invention reduces loss of boric acid from 5.94-7.09 to 4.73-5.49%. EFFECT: increased yield of product. Изобретение относится к получению борной кислоты сернокислотным методом из боросиликатного сырья с содержанием железа более 2%. Датолитовый концентрат, содержащий 2,0 - 5,51% FeO, смешивают с оборотными растворами и серной кислотой. После перемешивания и выдержки пульпы при 105 - 107C в течение 90 мин в нее добавляют оборотные растворы и нейтрализуют пульпу введением прокаленной датолитовой руды и бората кальция. Пульпу выщелачивают при 65C в течение 45 мин, затем отфильтровывают с получением продукционного раствора и шлама. Шлам промывают водой и одновременно с промывкой ведут обработку газом, содержащим углекислоту до pH 6,15 - 6,40. Пульпу отфильтровывают. Изобретение позволяет снизить потери борной кислоты за счет недоотмывки при переработке сырья с содержанием железа более 2,0% с 5,94 - 7,09% до 4,73 - 5,49%. 1 табл.