METHOD OF POLYIMIDE SYNTHESIS

FIELD: high-molecular compounds, organic chemistry. SUBSTANCE: method involves the low-temperature polycondensation of aminophenoxyphthalic acid derivative in aprotonic polar solvent followed by forming artile from reactive solution and imidization at heating. Derivative of aminophenoxyphthalic acid is 4-(3′-aminophenoxy)-phthalic acid which is heated at 180-190 C for 6-9 hr before polycondensation. Synthesized polyimide shows decomposition point at 210-215 C, rupture strength is 140-160 MPa, rupture elongation is 15-170%, decomposition point onset is 440-450 C, adhesion to glass and steel is 5.6-7.5 and 5.5-6.0 kg/cm, respectively. EFFECT: improved adhesion properties, solubility and softening of polyimide. 2 tbl Изобретение относится к способам получения высокомолекулярных соединений, конкретно к способу получения термостойких, растворимых и размягчаемых полиимидов, которые могут найти широкое применение в качестве термостойких конструкционных и электроизоляционных материалов в различных областях техники. Изобретение позволяет улучшить адгезионные характеристики и придает полиимиду растворимость и способность к размягчению за счет того, что в способе получения полиимида низкотемпературной поликонденсацией производного аминофеноксифталевой кислоты в апротонном полярном растворителе с последующим формованием из реакционного раствора изделия и имидизацией при нагревании в качестве производного аминофеноксифталевой кислоты используют 4-(3′) -(аминофенокси) фталевую кислоту и перед поликонденсацией ее нагревают при 180 - 190С в течение 6 - 9 ч. Получаемый полиимид имеет температуру размягчения 210 - 215С, прочность при разрыве 140 - 160 МПа, удлинение при разрыве 15 - 170%, температуру начала разложения 440 - 450С и адгезию к стеклу и стали, равную 5,6 - 7,5 и 5,5 - 6,0 кг/см соответственно. 2 табл.