SOLUTION FOR CHEMICAL NICKEL-PLATING OF MAGNESIUM

FIELD: chemical nickel plating. SUBSTANCE: chemical nickel plating solution contains, g/l: nickel sulfate 10-20; sodium hypophosphite 10-15; sodium fluorine 10-15; sodium citrate 10-20; sodium salt as stabilizing additive, particularly, m-nitrobenzenesulfonic acids (ludigol) 0.01-0.20. Usage of ludi...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	Baraboshkina N.K, Jalyshev A.V, Vasil'eva T.P, Voronina T.P, Piskarev V.I, Krasnosel'skaja N.V, Ryzhukhina Z.K, Novozhilova L.I, Fedorov P.I
Format:	Patent
Sprache:	eng ; rus
Schlagworte:	CHEMICAL SURFACE TREATMENT CHEMISTRY COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATIONOR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY IONIMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL COATING MATERIAL WITH METALLIC MATERIAL COATING METALLIC MATERIAL DIFFUSION TREATMENT OF METALLIC MATERIAL INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION INGENERAL METALLURGY SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THESURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	FIELD: chemical nickel plating. SUBSTANCE: chemical nickel plating solution contains, g/l: nickel sulfate 10-20; sodium hypophosphite 10-15; sodium fluorine 10-15; sodium citrate 10-20; sodium salt as stabilizing additive, particularly, m-nitrobenzenesulfonic acids (ludigol) 0.01-0.20. Usage of ludigol as stabilizing additive allows corrosion-resistant coat on magnesium powder to be obtained at room temperature, while nickel-plating by means of analogous solution is conducted at 50-60 C and by means of prototype solution at 94-100 C. EFFECT: increased efficiency and high quality of corrosion- resistant coat. 1 tbl Изобретение относится к области химического никелирования порошкообразных материалов, в частности порошка магния. Цель изобретения - снижение температуры процесса. Раствор для химического никелирования содержит, г/л: никель сернокислый 10 - 20, гипофосфат натрия 10 - 20, натрий фтористый 10 - 15, натрий лимоннокислый 10 - 20 и в качестве стабилизирующей добавки - натриевую соль -нитробензол сульфокислоты (лудигол) 0,01 - 0,20. Использование лудигона в качестве стабилизирующей добавки обеспечивает возможность получения коррозионностойкого покрытия на магниевом порошке при комнатной температуре никелирования из раствора - аналога ведут при 50 - 60С, а из раствора - прототипа - при 94 - 100С. 1 табл.