Process for producing a grain-orientated electrical steel sheet

The invention relates to a process for producing a grain-orientated electrical steel sheet in which a steel slab is soaked at a temperature which is lower than the solubility temperature for manganese sulphide but above the solubility temperature for copper sulphide. The slab is subsequently hot-rolled at a starting temperature of at least 960 °C and at an end temperature in the range of 880 to 1000 °C to provide a hot-strip final thickness in the range of 1.5 to 7.0 mm. The hot strip is subsequently annealed at a temperature in the range of 880 to 1150 °C and cooled at a rate of above 15 K/s. The hot strip is cold rolled in one or a plurality of cold rolling stages. There follows recrystallisating annealing with simultaneous decarburisation, application of a separating agent, high temperature annealing and, after application of an insulating layer, final annealing. The invention is characterised in that the cold strip for high-temperature annealing is heated in an atmosphere containing less than 25 vol. % of H2, the remainder being nitrogen and /or a noble gas, at least until the critical temperature is obtained. Oceľový plát s orientovaným zrnením a definovaným zložením je zahrievaný, valcovaný, žíhaný a okamžite ochladený, následne valcovaný za studena v jednom alebo viacerých krokoch, pričom studený pruh sa podrobí rekryštalizačnému žíhaniu vo vlhkej atmosfére s obsahom vodíka a dusíka pri súčasnom odstránení uhlíka. Po aplikácii separačného činidla so základným obsahom MgO na obe strany je žíhaný pri vysokej teplote a po aplikácii izolačnej vrstvy sa podrobí výslednému žíhaniu, pričom studený pruh pre vysokotepelné žíhanie sa zahrieva v atmosfére tvorenej menej ako 25 objemových % H2, zvyšok je dusík a/alebo vzácny plyn, ako je argón, až do dosiahnutia udržiavacej teploty 1150 až 1 200 °C, výhodne 1 180 °C.ŕ