METHOD FOR SOLDERING ZIRCONIUM WITH CONSTRUCTIONAL METAL

FIELD: mechanical engineering. SUBSTANCE: method involves regulating process of interaction between zirconium with solder and metal to be soldered by double-staged forming of joint: creation of liquid metal barrier layer of low-melting temperature zirconium base metal at the first stage and vacuum soldering of tinned zirconium with other constructional metal at predetermined temperature- time range (973-1073 K and 1-3 min) for enabling dispersion of constructional metal in low-melting temperature solder with following cooling of mixed joint at second stage. EFFECT: increased efficiency, improved quality of soldered joints of zirconium with number of constructional metals. 2 cl Изобретение относится к области машиностроения, в частности к способам пайки разнородных соединений циркония. Цель изобретения - повышение качества паяных соединений циркония с рядом конструкционных металлов. Цель достигается путем регулирования процесса взаимодействия циркония с припоем и паяемым металлом. Последнее достигается за счет двухэтапности образования соединения: создания жидкометаллического барьерного слоя из легкоплавкого металла на цирконии - на первом этапе, и процесс пайки облуженного циркония с другим конструкционным металлом в вакууме в заданном температурно-временном диапазоне (973-1073 K и 1- 3 мин), обеспечивающем условия для диспергирования конструкционного металла в легкоплавком припое с последущим охлаждением разнородного соединения, - на втором.