HIGH STRENGTH CORROSION RESISTANT POWDER STEEL

FIELD: iron and steel industry.SUBSTANCE: invention relates to the field of ferrous metallurgy, namely to the production of powder corrosion-resistant martensitic-aging steel used in technologies for the additive production of power elements of gas turbine engines operated at temperatures from -70 to +550°C. Steel contains components in the following ratio, weight percentage: chromium 12.50-13.50, nickel 4.50-5.50, molybdenum 3.50-4.50, cobalt 8.50-9.50, manganese no more than 0.30, silicon no more than 0.10, niobium 0.08-0.15, yttrium no more than 0.02, lanthanum no more than 0.02, carbon no more than 0.02, sulfur no more than 0.01, oxygen no more than 0.06, iron the rest. Steel has a tensile strength of no less than 1400 MPa, a yield strength of no less than 1170 MPa, a relative elongation of no less than 14%, a transverse narrowing of no less than 50%.EFFECT: new high strength steel is obtained.1 cl Изобретение относится к области черной металлургии, а именно к производству порошковой коррозионно-стойкой мартенситно-стареющей стали, используемой в технологиях аддитивного производства силовых элементов газотурбинных двигателей, эксплуатирующихся при температурах от минус 70 до плюс 550°С. Сталь содержит компоненты в следующем соотношении, мас.%: хром 12,50-13,50, никель 4,50-5,50, молибден 3,50-4,50, кобальт 8,50-9,50, марганец не более 0,30, кремний не более 0,10, ниобий 0,08-0,15, иттрий не более 0,02, лантан не более 0,02, углерод не более 0,02, сера не более 0,01, кислород не более 0,06, железо - остальное. Сталь обладает пределом прочности не менее 1400 МПа, пределом текучести не менее 1170 МПа, относительным удлинением не менее 14%, поперечным сужением не менее 50%. 1 з.п. ф-лы, 2 табл.