METHOD OF LOCAL HEAT TREATMENT OF WELDED JOINTS

FIELD: metallurgy.SUBSTANCE: invention relates to metallurgy and can be used for local heat treatment of welded joints of large-sized products. The method of local heat treatment of welded joints of large-sized products includes heating the welded joint zone, holding at a given temperature and cooling. Heating of the welded joint zone is carried out first to a temperature of 300 °C at a rate of no more than 40 °C/h, then to a temperature in the range of 620-660 °C at a rate of no more than 30 °C/h, while holding is performed at this temperature for 8-10 hours for final tempering, cooling is carried out to a temperature of 300 °C at a rate of not more than 30 °C/h, and subsequent cooling is performed in air to a temperature below 50 °C.EFFECT: increased strength and plastic properties of welded joints of products, excluded significant temperature deformations during heat treatment of products with complex internals.1 cl Изобретение относится к металлургии и может быть использовано для местной термической обработки сварных соединений крупногабаритных изделий. Способ местной термической обработки сварных соединений крупногабаритных изделий включает нагрев зоны сварного соединения, выдержку при данной температуре и охлаждение. Нагрев зоны сварного соединения осуществляют сначала до температуры 300°С со скоростью не более 40°С/ч, затем до температуры в диапазоне 620-660°С со скоростью не более 30°С/ч, при этом выдержку выполняют при данной температуре в течение 8-10 ч для окончательного отпуска, охлаждение осуществляют до температуры 300°С со скоростью не более 30°С/ч, а последующее охлаждение выполняют на воздухе до температуры ниже 50°C. Обеспечивается повышение прочностных и пластических свойств сварных соединений изделий, исключаются значительные температурные деформации при термообработке изделий со сложными внутрикорпусными устройствами.