Glass melting component

FIELD: glass melting.SUBSTANCE: invention relates to a method for producing a glass melting component, as well as the glass melting component. A method for producing a glass melting component that consists of a refractory metal in which the surface area of the glass melting component is compacted, at least partially, by applying a local compressive force. As a result, its porosity decreases in comparison with the volume part, which is located below the surface zone and has a residual porosity. After compacting the surface area, the glass melting component, or at least the surface area of the glass melting component, is heat-treated at a temperature higher than the recrystallization temperature of the refractory metal, so that grain growth is caused in the surface area.EFFECT: technical result is the provision of a method for producing a component for glass melting, which consists of a refractory metal with high resistance to glass melts.14 cl, 5 tbl, 10 dwg Изобретения относятся к способу получения компонента для варки стекла, а также к компоненту для варки стекла. Способ получения компонента для варки стекла, который состоит из тугоплавкого металла, в котором поверхностную зону компонента для варки стекла уплотняют, по меньшей мере частично, путем приложения локального сжимающего усилия. В результате ее пористость уменьшается по сравнению с объемной частью, которая расположена ниже поверхностной зоны и обладает остаточной пористостью. После уплотнения поверхностной зоны компонент для варки стекла или по меньшей мере поверхностную зону компонента для варки стекла подвергают термообработке при температуре выше температуры рекристаллизации тугоплавкого металла, так что вызывают рост зерен в поверхностной зоне. Технический результат - обеспечение способа получения компонента для варки стекла, состоящего из тугоплавкого металла, обладающего повышенной стойкостью к расплавам стекла. 3 н. и 11 з.п. ф-лы, 5 табл., 10 ил.